SABIC® COHERE™ S100L

Polyolefin Plastomer

Saudi Basic Industries Corporation (SABIC)

产品说明：

SABIC® COHERE™ S100L  is a ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has excellent processability.
SABIC® COHERE™ S100L does contain Slip and Antiblock.
Applications
Typical application for SABIC® COHERE™ S100L is low temperature sealing layer for high value packaging (low SIT, seal through contamination, toughness improvement).

物性信息：

基本信息
添加剂	抗结块剂 增滑剂
特性	Excellent Processability 共聚物 光滑性 抗结块性 辛烯共聚单体
用途	Blown Film 包装
加工方法	吹塑薄膜

物理性能	额定值	单位制	测试方法
密度	0.902	g/cm3	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	50	μm
割线模量			ASTM D882
1% 正割, MD	68.0	MPa	ASTM D882
1% 正割, TD	76.0	MPa	ASTM D882
抗张强度			ASTM D882
MD : 断裂	47.0	MPa	ASTM D882
TD : 断裂	42.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂	600	%	ASTM D882
TD : 断裂	620	%	ASTM D882
落锤冲击 1	> 1000	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD	10	g	ASTM D1922
TD	17	g	ASTM D1922

热性能	额定值	单位制	测试方法
熔融温度	100	°C	内部方法

光学性能	额定值	单位制	测试方法
雾度	4.0	%	ASTM D1003

补充信息	额定值	单位制
Blown Film Melt Temperature	180 到 200	°C
Blow-up Ratio	2.00 到 3.00
Properties have been measured on blown film of 50 μm and BUR = 2.5

备注
1 .	F50