Pro-fax SA861

Polypropylene Random Copolymer

LyondellBasell Industries

产品说明：

Pro-fax SA-861 polypropylene random copolymer resin, formulated with slip and antiblock, is designed for cast film packaging applications. Cast film made with this resin has exceptional clarity and gloss, as well as improved cold temperature impact resistance and broader heat seal range compared to homopolymer polypropylene.
Typical applications include bags for hosiery, shirts and other textiles, produce packaging, sheet protectors, photograph pockets and card display sleeves.
For regulatory compliance information see Pro-fax SA861 Regulatory Affairs Product Stewardship Information/Certification Data Sheet (RAPIDS).

物性信息：

基本信息
添加剂	抗结块剂 增滑剂
特性	高光 光滑性 光学性能 抗结块性 可热封 清晰度，高 无规共聚物
用途	包装 薄膜 袋子 流延薄膜 食品包装
形式	粒子
加工方法	流延薄膜

物理性能	额定值	单位制	测试方法
比重	0.900	g/cm3	ASTM D792B
熔流率（熔体流动速率） (230°C/2.16 kg)	6.5	g/10 min	ASTM D1238

机械性能	额定值	单位制	测试方法
抗张强度 (屈服)	27.6	MPa	ASTM D638
伸长率 (屈服)	13	%	ASTM D638
弯曲模量 - 1% 正割 1	896	MPa	ASTM D790A
摩擦系数	0.15 到 0.25		ASTM D1894

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	25	μm
割线模量			ASTM D882
1% 正割, MD : 25 μm	655	MPa	ASTM D882
1% 正割, TD : 25 μm	621	MPa	ASTM D882
抗张强度			ASTM D882
MD : 屈服, 25 μm	49.0	MPa	ASTM D882
TD : 屈服, 25 μm	32.4	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 25 μm	730	%	ASTM D882
TD : 断裂, 25 μm	710	%	ASTM D882
落锤冲击			ASTM D1709
0°C, 25 μm	360	g	ASTM D1709
23°C, 25 μm	1900	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 25 μm	25	g	ASTM D1922
TD : 25 μm	500	g	ASTM D1922
始封温度 (25 μm)	135	°C
Dart Drop Test			ASTM D1709
0°C, 25.0 μm	35.6	J/cm	ASTM D1709
23°C, 25.0 μm	187	J/cm	ASTM D1709

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (23°C)	69	J/m	ASTM D256A

热性能	额定值	单位制	测试方法
载荷下热变形温度 (0.45 MPa, 未退火)	76.1	°C	ASTM D648

光学性能	额定值	单位制	测试方法
光泽度 (45°, 25.0 μm)	80 到 85		ASTM D2457
雾度 (25.0 μm)	3.0	%	ASTM D1003

备注
1 .	1.0 mm/min