Elvax 型号
|
熔融指数
|
%VA含量
|
拉伸强度 Mpa(ASTM D 17083)
|
断裂伸长率,%(ASTM D 17083)
|
|
Elvax 40 W
|
52
|
40
|
5.2-6.2
|
1000-1300
|
|
Elvax 40 L
|
3
|
40
|
11
|
1270
|
|
Elvax 140 W
|
400
|
33
|
1.7-3.1
|
800-1000
|
|
Elvax 150 W
|
43
|
32
|
6.9-8.3
|
900-1100
|
|
Elvax 170
|
0.8
|
35
|
11
|
1400
|
|
Elvax 200 W
|
2500
|
28
|
1.6
|
90
|
|
Elvax 205 W
|
800
|
28
|
2.6
|
400-600
|
|
Elvax 210 W
|
400
|
28
|
2.8
|
800-1000
|
|
Elvax 220 W
|
150
|
28
|
5.5
|
800-1000
|
|
Elvax 240 W
|
43
|
28
|
9.7
|
800-1000
|
|
Elvax 250 W
|
25
|
28
|
11
|
800-1000
|
|
Elvax 260
|
6
|
28
|
24
|
800-1000
|
|
Elvax 265
|
3
|
28
|
29
|
800-1000
|
|
Elvax 310
|
400
|
25
|
3.3
|
800-1000
|
|
Elvax 350
|
19
|
25
|
14
|
800-1000
|
|
Elvax 360
|
2
|
25
|
26
|
800-1000
|
|
Elvax 410
|
500
|
18
|
4.7
|
600-900
|
|
Elvax 420
|
150
|
18
|
8.6
|
600-900
|
|
Elvax 450
|
8
|
18
|
18
|
600-900
|
|
Elvax 460
|
2.5
|
18
|
23
|
600-900
|
|
Elvax 470
|
0.7
|
18
|
26
|
600-900
|
|
Elvax 500 W
|
2500
|
14
|
5
|
90
|
|
Elvax 550
|
8
|
15
|
18
|
800-900
|
|
Elvax 560
|
2.5
|
15
|
22
|
800-900
|
|
Elvax 650Q
|
8
|
12
|
17
|
750-850
|
|
Elvax 660
|
2.5
|
12
|
21
|
750-850
|
|
Elvax 670
|
0.35
|
12
|
26
|
750-850
|
|
Elvax 750
|
7
|
9
|
15
|
600-750
|
|
Elvax 760
|
2
|
9.3
|
21
|
600-750
|
|
Elvax 770
|
0.8
|
9.5
|
22
|
600-750
|
|
Elvax 880
|
1.2
|
7.5
|
21
|
600-750
|
EVA广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。
1、乙酸乙烯含量在5%以下的EVA，其主要产品是薄膜、电线电缆、LDPE改性剂、胶粘剂等；
2、乙酸乙烯含量在5%~10% 的EVA产品为弹性薄膜等；
3、乙酸乙烯含量在20~28%的EVA，主要用于热熔粘合剂和涂层制品；
EVA是由LLDPE（线性低密度聚乙烯）和醋酸（VA）共聚而成。
乙烯-醋酸乙烯共聚物，简称EVA。一般醋酸乙烯（VA）的含量在5%-40%，与聚乙烯（PE)相比，EVA由于在分子链中引入醋酸乙烯单体，从而降低了高结晶度，提高了韧性、抗冲击性、填料相溶性和热密封性能，被广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域.