HDPE M40060S SABIC® HDPE M40060S
  • 价格: ¥11.00/千克
  • 发布日期: 2023-06-14
  • 更新日期: 2024-06-21
产品详请
特性级别 标准级|||
牌号 M40060S
型号 M40060S
加工级别 注塑级|||
品名 HDPE
用途级别 通用级|||

SABIC® HDPE M40060S

High Density Polyethylene Copolymer
Saudi Basic Industries Corporation (SABIC)
产品说明:
SABIC® HDPE M40060S is an UV stabilized, high density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It has improved mouldability. Articles produced from this grade typically show good impact strength, low warpage, stress crack resistance (ESCR) and good gloss.
Typical applications.
SABIC® HDPE M40060S is typically used for the manufacture of injection moulded articles such as pails, shipping containers and industrial parts.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
物性信息:
基本信息
添加剂
  • 紫外线稳定剂
特性
  • 低翘曲性
  • 高 ESCR(抗应力开裂)
  • 高密度
  • 共聚物
  • 光泽,中
  • 抗撞击性,良好
  • 抗紫外线性能良好
  • 窄分子量分布
用途
  • 工业部件
  • 装运容器
加工方法
  • 注射成型
物理性能 额定值 单位制 测试方法
密度 0.960 g/cm3 ISO 1183
熔流率(熔体流动速率) ISO 1133
    190°C/2.16 kg 4.0 g/10 min ISO 1133
    190°C/5.0 kg 11 g/10 min ISO 1133
抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型) 70.0 hr 内部方法
硬度 额定值 单位制 测试方法
肖氏硬度 (邵氏 D, 模压成型) 64 ISO 868
机械性能 额定值 单位制 测试方法
拉伸模量 (2.00 mm, 模压成型) 1300 MPa ISO 527-2/1BA/50
拉伸应力 ISO 527-2/1BA/50
    屈服, 2.00 mm, 模压成型 30.0 MPa ISO 527-2/1BA/50
    断裂, 2.00 mm, 模压成型 24.0 MPa ISO 527-2/1BA/50
拉伸应变 (断裂, 2.00 mm, 模压成型) > 200 % ISO 527-2/1BA/50
弯曲模量 (2.00 mm, 模压成型) 1500 MPa ISO 178
弯曲应力 (2.00 mm, 模压成型) 30.0 MPa ISO 178
冲击性能 额定值 单位制 测试方法
悬壁梁缺口冲击强度 (23°C, 模压成型) 5.0 kJ/m2 ISO 180/A
热性能 额定值 单位制 测试方法
热变形温度 (0.45 MPa, 未退火) 90.0 °C ISO 75-2/B
维卡软化温度 127 °C ISO 306/A
溶融温度(DSC) 133 °C ISO 11357-3
Enthalpy Change 219 J/g ISO 11357-3
注射 额定值 单位制
加工(熔体)温度 232 到 260 °C
模具温度 20.0 到 40.0 °C
注塑压力 93.0 到 103 MPa
备注
1 . 2 MPa