食品包装Moplen HP425J 均聚物PP HP425J 利安德巴塞尔PP HP425J
- 价格： ￥11.00/千克
- 发布日期： 2019-04-08
- 更新日期： 2025-07-22
产品详请
| 特性级别 |
标准级|||
|
| 牌号 |
HP423M
|
| 加工级别 |
注塑级|||
|
| 品名 |
|
| 厂家(产地) |
利安德巴塞尔
|
| 用途级别 |
通用级|||
|
Moplen HP425J
聚丙烯均聚物
PolyMirae
产品说明：
Moplen HP425J is a modified polypropylene homopolymer containing a Calcium Stearate free stabilization package. It does not contain any slip or antiblocking additives.
Moplen HP425J is designed for the high speed production of BOPP films. It is used by customers for a broad range of applications including metallizable films and both plain and coextruded structures.
BOPP films produced with Moplen HP425J exhibit balanced mechanical properties, good transparency, gloss and enhanced shrinkage properties.
For regulatory information please refer to Moplen HP425J Product Stewardship Bulletin (PSB).
Moplen HP425J 物性表
| 基本信息 |
|
|---|
| 特性 | |
| 用途 | Bi-axially Oriented Film 包装 薄膜 食品包装
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 0.900 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 肖氏硬度 (邵氏 D) | 70 |
| ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 | 1450 | MPa | ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服 | 33.0 | MPa | ASTM D638 |
| 屈服 | 34.0 | MPa | ISO 527-2/50 |
| 伸长率 |
|
|
|
| 屈服 | 11 | % | ASTM D638 |
| 屈服 | 10 | % | ISO 527-2/50 |
| 断裂 | 410 | % | ISO 527-2/50 |
| 弯曲模量 | 1400 | MPa | ASTM D790 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 - 正切 1(20 μm) | 2400 | MPa | MA 18068 |
| 拉伸应力 2(断裂, 20 μm) | 116 | MPa | MA 18068 |
| 伸长率 3(断裂, 20 μm) | 29 | % | MA 18068 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 | 330 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火 | 93.0 | °C | ASTM D648 |
| 0.45 MPa, 未退火 | 88.0 | °C | ISO 75-2/B |
| 维卡软化温度 | 152 | °C | ISO 306/A50 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 雾度 (20.0 μm) | 0.50 | % | ASTM D1003 |
| 备注 |
|---|
| 1 . | 5 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |