韩国三星PP BI830 高抗冲击PP BI830 Hanwha Total PP BI830
- 价格： ￥13.00/千克
- 发布日期： 2019-03-07
- 更新日期： 2025-07-25
产品详请
| 特性级别 |
透明级|||标准级|||高抗冲|||
|
| 牌号 |
BI830
|
| 加工级别 |
注塑级|||
|
| 品名 |
|
| 厂家(产地) |
三星
|
| 用途级别 |
通用级|||
|
Hanwha Total PP BI830
高结晶性聚丙烯
HANWHA TOTAL PETROCHEMICALS Co., Ltd.
产品说明：
BI830 is a highly isotactic block copolymer with high flowability, high strength, and high crystallinity compared to general PP, and is an RTPO (Reactor made Thermoplastic Polymer Olefin) with a high content of ethylene-propylene rubber. It shows an excellent balance of impact resistance (room temperature Izod NB) and strength due to high crystalline technology and the most appropriate rubber design. BI830 has high flowability due to its high melt index, making the product useful in automobile bumpers and the corresponding compound material for large scale parts.
Hanwha Total PP BI830 物性表
| 基本信息 |
|
|---|
| 特性 | Block Copolymer 超高抗冲击性 高强度 间苯二甲 结晶 流动性高 耐低温冲击 耐热性，高
|
| 用途 | 电器用具 家用货品 汽车防撞杆 汽车内部零件 汽车内部装备 汽车仪表板 食品容器 室外应用
|
| 形式 | |
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 密度 | 0.910 | g/cm3 | ASTM D1505 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 (R 级) | 40 |
| ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 (屈服) | 18.6 | MPa | ASTM D638 |
| 伸长率 (断裂) | 75 | % | ASTM D638 |
| 弯曲模量 | 834 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 |
|
| ASTM D256 |
| -20°C | 98 | J/m | ASTM D256 |
| 23°C | 590 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 (0.45 MPa, 未退火) | 98.0 | °C | ASTM D648 |
| 光学性能 | 额定值 |
| 测试方法 |
|---|
| 光泽度 | 60 |
| ASTM D2457 |
| 补充信息 |
|---|
| Dupont Impact Strength, SAMSUNG TOTAL, -20°C: 500 kg/cm |
| 注射 | 额定值 | 单位制 |
|
|---|
| 料筒后部温度 | 160 到 200 | °C |
|
| 料筒中部温度 | 200 到 240 | °C |
|
| 料筒前部温度 | 220 到 260 | °C |
|
| 模具温度 | 30.0 到 50.0 | °C |
|
| 注塑压力 | 98.1 到 245 | MPa |
|
| 保压 | 78.5 到 226 | MPa |
|